Organophotoreceptors with azine-based compounds

ABSTRACT

Improved organophotoreceptor comprises an electrically conductive substrate and a photoconductive element on the electrically conductive substrate, the photoconductive element comprising:  
     a) a charge transport material having the formula,  
                 
 
     where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent; and  
     (b) a charge generating compound.  
     Corresponding electrophotographic apparatuses and imaging methods are described.

CROSS REFERENCE TO RELATED APPLICATION

[0001] This application claims priority to copending U.S. Provisional Patent Application serial No. 60/466,813 to Jubran et al., filed on Apr. 30, 2003, and entitled “Organophotoreceptors With Azine-Based Compounds,” incorporated herein by reference.

FIELD OF THE INVENTION

[0002] This invention relates to organophotoreceptors suitable for use in electrophotography and, more specifically, to an organophotoreceptors having an azine compound comprising an arylamine group and a 9-fluorenylidene group having at least a solubilizing substituent.

BACKGROUND OF THE INVENTION

[0003] In electrophotography, an organophotoreceptor in the form of a plate, disk, sheet, belt, drum or the like having an electrically insulating photoconductive element on an electrically conductive substrate is imaged by first uniformly electrostatically charging the surface of a photoconductive element, and then exposing the charged surface to a pattern of light. The light exposure selectively dissipates the charge in the illuminated areas where light strikes the surface, thereby forming a pattern of charged and uncharged areas referred to as a latent image. A liquid toner or solid toner can then be provided in the vicinity of the latent image, and toner droplets or particles can be deposited in either the charged or uncharged areas depending on the properties of the toner to create a toned image on the surface of the photoconductive element. The resulting toned image can be transferred to a suitable ultimate or intermediate receiving surface, such as paper, or the photoconductive element can operate as the ultimate receptor for the image. The imaging process can be repeated many times to complete a single image, which can involve, for example, overlying images of distinct color components or effecting shadow images to complete a full color complete image, and/or to reproduce additional images.

[0004] Both single layer and multilayer photoconductive elements have been used. In the single layer embodiment, charge generating compound and a charge transport material selected from the group consisting of a charge transport compound, an electron transport compound, and a combination of both are combined with a polymeric binder and then deposited on the electrically conductive substrate. In the multilayer embodiments based on a charge transport compound, the charge transport compound and charge generating compound are in the form of separate layers, each of which can optionally be combined with a polymeric binder, deposited on the electrically conductive substrate. Two arrangements are possible. In one arrangement (the “dual layer” arrangement), the charge generating layer is deposited on the electrically conductive substrate and the charge transport layer is deposited on top of the charge generating layer. In an alternate arrangement (the “inverted dual layer” arrangement), the order of the charge transport layer and charge generating layer is reversed.

[0005] In both the single and multilayer photoconductive elements, the purpose of the charge generating material is to generate charge carriers (i.e., holes and/or electrons) upon exposure to light. The purpose of the charge transport material is to accept these charge carriers and transport them through the charge transport layer in order to discharge a surface charge on the photoconductive element. The charge transport material can be a charge transport compound, an electron transport compound, or a combination of both. When a charge transport compound is used, the charge transport compound accepts the hole carriers and transports them through the layer in which the charge transport compound is located. When an electron transport compound is used, the electron transport compound accepts the electron carriers and transports them through the layer in which the electron transport compound is located.

[0006] The charge transport material is preferred to be compatible with polymeric binders and to have good solubility in organic solvents for the processing and manufacturing of the organophotoreceptor. However, most charge transport materials are aromatic and conjugated. Consequently, they are rigid compounds that may not be sufficiently compatible with the polymeric binders and may not be sufficiently soluble in organic solvents for easy processing.

SUMMARY OF THE INVENTION

[0007] This invention provides organophotoreceptors having good electrostatic properties such as high V_(acc) and low V_(dis). This invention also provides charge transport materials having an increased compatibility with polymeric binders and an improved solubility in organic solvents for processing.

[0008] In a first aspect, the invention pertains to an organophotoreceptor comprising an electrically conductive substrate and a photoconductive element on the electrically conductive substrate, the photoconductive element comprising: a) a charge transport material having the following formula:

[0009] where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group such as a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent comprising a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group; and

[0010] (b) a charge generating compound.

[0011] The organophotoreceptor may be provided, for example, in the form of a plate, a flexible belt, a flexible disk, a sheet, a rigid drum, or a sheet around a rigid or compliant drum. In one embodiment, the organophotoreceptor includes: (a) a photoconductive element comprising the charge transport material, the charge generating compound, optionally a second charge transport material, and optionally a polymeric binder; and (b) the electrically conductive substrate.

[0012] In a second aspect, the invention features an electrophotographic imaging apparatus that comprises (a) a light imaging component; and (b) the above-described organophotoreceptor oriented to receive light from the light imaging component. The apparatus can further comprise a toner dispenser. The method of electrophotographic imaging with photoreceptors containing the above noted charge transport material is also described.

[0013] In a third aspect, the invention features an electrophotographic imaging process that includes (a) applying an electrical charge to a surface of the above-described organophotoreceptor; (b) imagewise exposing the surface of the organophotoreceptor to radiation to dissipate charge in selected areas and thereby form a pattern of at least relatively charged and uncharged areas on the surface; (c) contacting the surface with a toner, such as a liquid toner that includes a dispersion of colorant particles in an organic liquid, to create a toned image; and (d) transferring the toned image to a substrate.

[0014] In a fourth aspect, the invention features a charge transport material having Formula (1) above.

[0015] The invention provides suitable charge transport materials for organophotoreceptors featuring a combination of good mechanical, electrostatic, and solubility properties. These photoreceptors can be used successfully with toners, such as liquid toners and dry toners, to produce high quality images. The high quality of the imaging system can be maintained after repeated cycling.

[0016] Other features and advantages of the invention will be apparent from the following description of the specific embodiments thereof, and from the claims.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0017] An organophotoreceptor as described herein has an electrically conductive substrate and a photoconductive element comprising a charge generating compound and a charge transport material having an arylamine group, such as a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group, and a 9-fluorenylidene group having at least a solubilizing substituent, such as a —(CH₂)_(n)H group. The 9-fluorenylidene group and the arylamine group are bonded through an azine linkage having the formula ═N—N═CR—. These charge transport materials have desirable properties as evidenced by their performance in organophotoreceptors for electrophotography. In particular, the charge transport materials of this invention have high charge carrier mobilities and good compatibility with various binder materials, and possess excellent electrophotographic properties. The organophotoreceptors according to this invention generally have a high photosensitivity, a low residual potential, and a high stability with respect to cycle testing, crystallization, and organophotoreceptor bending and stretching. The organophotoreceptors are particularly useful in laser printers and the like as well as fax machines, photocopiers, scanners and other electronic devices based on electrophotography. The use of these charge transport materials is described in more detail below in the context of laser printer use, although their application in other devices operating by electrophotography can be generalized from the discussion below.

[0018] To produce high quality images, particularly after multiple cycles, it is desirable for the charge transport materials to form a homogeneous solution with the polymeric binder and remain approximately homogeneously distributed through the organophotoreceptor material during the cycling of the material. In addition, it is desirable to increase the amount of charge that the charge transport material can accept (indicated by a parameter known as the acceptance voltage or “V_(acc)”), and to reduce retention of that charge upon discharge (indicated by a parameter known as the discharge voltage or “V_(dis)”).

[0019] The charge transport materials can be classified as a charge transport compound or an electron transport compound. There are many charge transport compounds and electron transport compounds known in the art for electrophotography. Non-limiting examples of charge transport compounds include, for example, pyrazoline derivatives, fluorene derivatives, oxadiazole derivatives, stilbene derivatives, enamine derivatives, enamine stilbene derivatives, hydrazone derivatives, carbazole hydrazone derivatives, (N,N-disubstituted)arylamines such as triaryl amines, polyvinyl carbazole, polyvinyl pyrene, polyacenaphthylene, or multi-hydrazone compounds comprising at least two hydrazone groups and at least two groups selected from the group consisting of (N,N-disubstituted)arylamine such as triphenylamine and heterocycles such as carbazole, julolidine, phenothiazine, phenazine, phenoxazine, phenoxathiin, thiazole, oxazole, isoxazole, dibenzo(1,4)dioxin, thianthrene, imidazole, benzothiazole, benzotriazole, benzoxazole, benzimidazole, quinoline, isoquinoline, quinoxaline, indole, indazole, pyrrole, purine, pyridine, pyridazine, pyrimidine, pyrazine, triazole, oxadiazole, tetrazole, thiadiazole, benzisoxazole, benzisothiazole, dibenzofuran, dibenzothiophene, thiophene, thianaphthene, quinazoline, or cinnoline.

[0020] Non-limiting examples of electron transport compounds include, for example, bromoaniline, tetracyanoethylene, tetracyanoquinodimethane, 2,4,7-trinitro-9-fluorenone, 2,4,5,7-tetranitro-9-fluorenone, 2,4,5,7-tetranitroxanthone, 2,4,8-trinitrothioxanthone, 2,6,8-trinitro-indeno [1,2-b]thiophene-4-one, and 1,3,7-trinitrodibenzo thiophene-5,5-dioxide, (2,3-diphenyl-1-indenylidene)malononitrile, 4H-thiopyran-1,1-dioxide and its derivatives such as 4-dicyanomethylene-2,6-diphenyl-4H-thiopyran-1,1-dioide, 4-dicyanomethylene-2,6-di-m-tolyl-4H-thiopyran-1,1-dioxide, and unsymmetrically substituted 2,6-diaryl-4H-thiopyran-1,1-dioxide such as 4H-1,1-dioxo-2-(p-isopropylphenyl)-6-phenyl-4-(dicyanomethylidene)thiopyran and 4H-1,1-dioxo-2-(p-isopropylphenyl)-6-(2-thienyl)-4-(dicyanomethylidene)thiopyran, derivatives of phospha-2,5-cyclohexadiene, alkoxycarbonyl-9-fluorenylidene)malononitrile derivatives such as (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile, (4-phenethoxycarbonyl-9-fluorenylidene)malononitrile, (4-carbitoxy-9-fluorenylidene)malononitrile, and diethyl(4-n-butoxycarbonyl-2,7-dinitro-9-fluorenylidene)-malonate, anthraquinodimethane derivatives such as 11,11,12,12-tetracyano-2-alkylanthraquinodimethane and 11,11-dicyano-12,12-bis(ethoxycarbonyl)anthraquinodimethane, anthrone derivatives such as 1-chloro-10-[bis(ethoxycarbonyl)methylene]anthrone, 1,8-dichloro-10-[bis(ethoxy carbonyl) methylene]anthrone, 1,8-dihydroxy-10-[bis(ethoxycarbonyl)methylene] anthrone, and 1-cyano-10-[bis(ethoxycarbonyl)methylene)anthrone, 7-nitro-2-aza-9-fluorenylidene-malononitrile, diphenoquinone derivatives, benzoquinone derivatives, naphtoquinone derivatives, quinine derivatives, tetracyanoethylenecyanoethylene, 2,4,8-trinitro thioxantone, dinitrobenzene derivatives, dinitroanthracene derivatives, dinitroacridine derivatives, nitroanthraquinone derivatives, dinitroanthraquinone derivatives, succinic anhydride, maleic anhydride, dibromo maleic anhydride, pyrene derivatives, carbazole derivatives, hydrazone derivatives, N,N-dialkylaniline derivatives, diphenylamine derivatives, triphenylamine derivatives, triphenylmethane derivatives, tetracyano quinoedimethane, 2,4,5,7-tetranitro-9-fluorenone, 2,4,7-trinitro-9-dicyanomethylene fluorenone, 2,4,5,7-tetranitroxanthone derivatives, and 2,4,8-trinitrothioxanthone derivatives. In some embodiments of interest, the electron transport compound comprises an (alkoxycarbonyl-9-fluorenylidene)malononitrile derivative, such as (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile.

[0021] Although there are many charge transport materials available, there is a need for other charge transport materials to meet the various requirements of particular electrophotography applications.

[0022] In electrophotography applications, a charge-generating compound within an organophotoreceptor absorbs light to form electron-hole pairs. These electrons and holes can be transported over an appropriate time frame under a large electric field to discharge locally a surface charge that is generating the field. The discharge of the field at a particular location results in a surface charge pattern that essentially matches the pattern drawn with the light. This charge pattern then can be used to guide toner deposition. The charge transport materials described herein are especially effective at transporting charge, and in particular holes from the electron-hole pairs formed by the charge generating compound. In some embodiments, a specific electron transport compound or charge transport compound can also be used along with the charge transport material of this invention.

[0023] The layer or layers of materials containing the charge generating compound and the charge transport materials are within an organophotoreceptor. To print a two dimensional image using the organophotoreceptor, the organophotoreceptor has a two dimensional surface for forming at least a portion of the image. The imaging process then continues by cycling the organophotoreceptor to complete the formation of the entire image and/or for the processing of subsequent images.

[0024] The organophotoreceptor may be provided in the form of a plate, a flexible belt, a disk, a rigid drum, a sheet around a rigid or compliant drum, or the like. The charge transport material can be in the same layer as the charge generating compound and/or in a different layer from the charge generating compound. Additional layers can be used also, as described further below.

[0025] In some embodiments, the organophotoreceptor material comprises, for example: (a) a charge transport layer comprising the charge transport material and a polymeric binder; (b) a charge generating layer comprising the charge generating compound and a polymeric binder; and (c) the electrically conductive substrate. The charge transport layer may be intermediate between the charge generating layer and the electrically conductive substrate. Alternatively, the charge generating layer may be intermediate between the charge transport layer and the electrically conductive substrate. In further embodiments, the organophotoreceptor material has a single layer with both a charge transport material and a charge generating compound within a polymeric binder.

[0026] The organophotoreceptors can be incorporated into an electrophotographic imaging apparatus, such as laser printers. In these devices, an image is formed from physical embodiments and converted to a light image that is scanned onto the organophotoreceptor to form a surface latent image. The surface latent image can be used to attract toner onto the surface of the organophotoreceptor, in which the toner image is the same or the negative of the light image projected onto the organophotoreceptor. The toner can be a liquid toner or a dry toner. The toner is subsequently transferred, from the surface of the organophotoreceptor, to a receiving surface, such as a sheet of paper. After the transfer of the toner, the surface is discharged, and the material is ready to cycle again. The imaging apparatus can further comprise, for example, a plurality of support rollers for transporting a paper receiving medium and/or for movement of the photoreceptor, a light imaging component with suitable optics to form the light image, a light source, such as a laser, a toner source and delivery system and an appropriate control system.

[0027] An electrophotographic imaging process generally can comprise (a) applying an electrical charge to a surface of the above-described organophotoreceptor; (b) imagewise exposing the surface of the organophotoreceptor to radiation to dissipate charge in selected areas and thereby form a pattern of charged and uncharged areas on the surface; (c) exposing the surface with a toner, such as a liquid toner that includes a dispersion of colorant particles in an organic liquid to create a toner image, to attract toner to the charged or discharged regions of the organophotoreceptor; and (d) transferring the toner image to a substrate.

[0028] As described herein, an organophotoreceptor comprises a charge transport material having the formula

[0029] where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent.

[0030] An arylamine group includes a p-(N,N-disubstituted)arylamine group (e.g., a triarylamine group, an alkyldiarylamine group, and a dialkylarylamine group), a julolidinyl group, and a carbazolyl group. The arylamine group may have more than one amine group, such as 2,4-bis(diphenylamino)phenyl group.

[0031] The 9-fluorenylidene group has at least a solubilizing substituent comprising a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group. The compatibility of a charge transport material with a particular binder can be estimated based on the difference between their Hildebrand solubility parameter values. If the difference is zero or small (5.0 MPa^(1/2)), the charge transport material will be compatible with the binder. However, if the difference is large (e.g. >5.0 MPa^(1/2)), the charge transport material may not be compatible with the binder. The calculation of Hildebrand solubility parameter can be found in Polymer Handbook, 3rd Ed., J. Brandrup & E. H. Immergut, John Wiley, NY, p. VII/522 (1989), incorporated herein by reference. The Hildebrand solubility parameters of the solubilizing substituent may be adjusted by replacing one or more of the methylene groups with other groups, such as those listed above. In general, solubilizing substituents with a wide range of Hildebrand solubility parameter may be formed by such a technique. In some embodiments, two adjacent methylene groups are replaced by an O atom and a C═O group to form an ester group. In other embodiments, two adjacent methylene groups are replaced by an NR₁ group and a C═O group to form an amide group. In further embodiments, two adjacent methylene groups are replaced by two CR₂ group to form an alkenyl solubilizing substituent.

[0032] The 9-fluorenylidene group may further include one or more substituents, in addition to the solubilizing substituent. Non-limiting examples of suitable substituent on the 9-fluorenylidene group include a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, an aromatic group, and a combination thereof.

[0033] An aromatic group can be any conjugated ring system containing 4n+2 pi-electrons. There are many criteria available for determining aromaticity. A widely employed criterion for the quantitative assessment of aromaticity is the resonance energy. In some embodiments, the resonance energy of the aromatic group is at least 10 KJ/mol. In further embodiments, the resonance energy of the aromatic group is greater than 0.1 KJ/mol. Aromatic groups may be classified as an aromatic heterocyclic group which contains at least a heteroatom in the 4n+2 pi-electron ring, or as an aryl group which does not contain a heteroatom in the 4n+2 pi-electron ring. The aromatic group may comprise a combination of aromatic heterocyclic group and aryl group. Nonetheless, either the aromatic heterocyclic or the aryl group may have at least one heteroatom in a substituent attached to the 4n+2 pi-electron ring. Furthermore, either the aromatic heterocyclic or the aryl group may comprise a monocyclic or polycyclic (such as bicyclic, tricyclic, etc.) ring.

[0034] Non-limiting examples of the aromatic heterocyclic group are furanyl, thiophenyl, pyrrolyl, indolyl, carbazolyl, benzofuranyl, benzothiophenyl, dibenzofuranyl, dibenzothiophenyl, pyridinyl, pyridazinyl, pyrimidinyl, pyrazinyl, triazinyl, tetrazinyl, petazinyl, quinolinyl, isoquinolinyl, cinnolinyl, phthalazinyl, quinazolinyl, quinoxalinyl, naphthyridinyl, pteridinyl, acridinyl, phenanthridinyl, phenanthrolinyl, anthyridinyl, purinyl, pteridinyl, alloxazinyl, phenazinyl, phenothiazinyl, phenoxazinyl, phenoxathiinyl, dibenzo(1,4)dioxinyl, thianthrenyl, and a combination thereof. The aromatic heterocyclic group may also include any combination of the above aromatic heterocyclic groups bonded together either by a bond (as in bicarbazolyl) or by a linking group (as in 1,6 di(10H-10-phenothiazinyl)hexane). The linking group may include an aliphatic group, an aromatic group, a heterocyclic group, or a combination thereof. Furthermore, either an aliphatic group or an aromatic group within a linking group may comprise at least one heteroatom such as O, S, Si, and N.

[0035] Non-limiting examples of the aryl group are phenyl, naphthyl, benzyl, or tolanyl group, sexiphenylene, phenanthrenyl, anthracenyl, coronenyl, and tolanylphenyl. The aryl group may also include any combination of the above aryl groups bonded together either by a bond (as in biphenyl group) or a linking group (as in stilbenyl, diphenyl sulfone, an arylamine group). The linking group may include an aliphatic group, an aromatic group, a heterocyclic group, or a combination thereof. Furthermore, either an aliphatic group or an aromatic group within a linking group may comprise at least one heteroatom such as O, S, Si, and N.

[0036] Substitution is liberally allowed on the chemical groups to affect various physical effects on the properties of the compounds, such as mobility, sensitivity, solubility, compatibility, stability, and the like, as is known generally in the art. In the description of chemical substituents, there are certain practices common to the art that are reflected in the use of language. The term group indicates that the generically recited chemical entity (e.g., alkyl group, alkenyl group, aromatic group, arylamine group, 9-fluorenylidene group, etc.) may have any substituent thereon which is consistent with the bond structure of that group. For example, where the term ‘alkyl group’ is used, that term would not only include unsubstituted linear, branched and cyclic alkyls, such as methyl, ethyl, isopropyl, tert-butyl, cyclohexyl, dodecyl and the like, but also substituents having heteroatom, such as 3-ethoxylpropyl, 4-(N,N-diethylamino)butyl, 3-hydroxypentyl, 2-thiolhexyl, 1,2,3-tribromoopropyl, and the like, and aromatic group, such as phenyl, naphthyl, carbazolyl, pyrrole, and the like. However, as is consistent with such nomenclature, no substitution would be included within the term that would alter the fundamental bond structure of the underlying group. For example, where a phenyl group is recited, substitution such as 2- or 4-aminophenyl, 2- or 4-(N,N-disubstituted)aminophenyl, 2,4-dihydroxyphenyl, 2,4,6-trithiophenyl, 2,4,6-trimethoxyphenyl and the like would be acceptable within the terminology, while substitution of 1,1,2,2,3,3-hexamethylphenyl would not be acceptable as that substitution would require the ring bond structure of the phenyl group to be altered to a non-aromatic form because of the substitution. Where the term moiety is used, such as alkyl moiety or phenyl moiety, that terminology indicates that the chemical moiety is not substituted. When referring to an alkyl moiety, the term represents only an unsubstituted alkyl hydrocarbon group, whether branched, straight chain, or cyclic.

[0037] Organophotoreceptors

[0038] The organophotoreceptor may be, for example, in the form of a plate, a sheet, a flexible belt, a disk, a rigid drum, or a sheet around a rigid or compliant drum, with flexible belts and rigid drums generally being used in commercial embodiments. The organophotoreceptor may comprise, for example, an electrically conductive substrate and on the electrically conductive substrate a photoconductive element in the form of one or more layers. The photoconductive element can comprise both a charge transport material and a charge generating compound in a polymeric binder, which may or may not be in the same layer, as well as a second charge transport material such as a charge transport compound or an electron transport compound in some embodiments. For example, the charge transport material and the charge generating compound can be in a single layer. In other embodiments, however, the photoconductive element comprises a bilayer construction featuring a charge generating layer and a separate charge transport layer. The charge generating layer may be located intermediate between the electrically conductive substrate and the charge transport layer. Alternatively, the photoconductive element may have a structure in which the charge transport layer is intermediate between the electrically conductive substrate and the charge generating layer.

[0039] The electrically conductive substrate may be flexible, for example in the form of a flexible web or a belt, or inflexible, for example in the form of a drum. A drum can have a hollow cylindrical structure that provides for attachment of the drum to a drive that rotates the drum during the imaging process. Typically, a flexible electrically conductive substrate comprises an electrically insulating substrate and a thin layer of electrically conductive material onto which the photoconductive material is applied.

[0040] The electrically insulating substrate may be paper or a film forming polymer such as polyester (e.g., polyethylene terephthalate or polyethylene naphthalate), polyimide, polysulfone, polypropylene, nylon, polyester, polycarbonate, polyvinyl resin, polyvinyl fluoride, polystyrene and the like. Specific examples of polymers for supporting substrates included, for example, polyethersulfone (STABAR™ S-100, available from ICI), polyvinyl fluoride (Tedlar®, available from E.I. DuPont de Nemours & Company), polybisphenol-A polycarbonate (MAKROFOL™, available from Mobay Chemical Company) and amorphous polyethylene terephthalate (MELINAR™, available from ICI Americas, Inc.). The electrically conductive materials may be graphite, dispersed carbon black, iodine, conductive polymers such as polypyrroles and Calgon® conductive polymer 261 (commercially available from Calgon Corporation, Inc., Pittsburgh, Pa.), metals such as aluminum, titanium, chromium, brass, gold, copper, palladium, nickel, or stainless steel, or metal oxide such as tin oxide or indium oxide. In embodiments of particular interest, the electrically conductive material is aluminum. Generally, the photoconductor substrate has a thickness adequate to provide the required mechanical stability. For example, flexible web substrates generally have a thickness from about 0.01 to about 1 mm, while drum substrates generally have a thickness from about 0.5 mm to about 2 mm.

[0041] The charge generating compound is a material that is capable of absorbing light to generate charge carriers, such as a dye or pigment. Non-limiting examples of suitable charge generating compounds include, for example, metal-free phthalocyanines (e.g., ELA 8034 metal-free phthalocyanine available from H.W. Sands, Inc. or Sanyo Color Works, Ltd., CGM-X01), metal phthalocyanines such as titanium phthalocyanine, copper phthalocyanine, oxytitanium phthalocyanine (also referred to as titanyl oxyphthalocyanine, and including any crystalline phase or mixtures of crystalline phases that can act as a charge generating compound), hydroxygallium phthalocyanine, squarylium dyes and pigments, hydroxy-substituted squarylium pigments, perylimides, polynuclear quinones available from Allied Chemical Corporation under the trade name INDOFAST™ Double Scarlet, INDOFAST™ Violet Lake B, INDOFAST™ Brilliant Scarlet and INDOFAST™ Orange, quinacridones available from DuPont under the trade name MONASTRAL™ Red, MONASTRAL™ Violet and MONASTRAL™ Red Y, naphthalene 1,4,5,8-tetracarboxylic acid derived pigments including the perinones, tetrabenzoporphyrins and tetranaphthaloporphyrins, indigo- and thioindigo dyes, benzothioxanthene-derivatives, perylene 3,4,9,10-tetracarboxylic acid derived pigments, polyazo-pigments including bisazo-, trisazo- and tetrakisazo-pigments, polymethine dyes, dyes containing quinazoline groups, tertiary amines, amorphous selenium, selenium alloys such as selenium-tellurium, selenium-tellurium-arsenic and selenium-arsenic, cadmium sulphoselenide, cadmium selenide, cadmium sulphide, and mixtures thereof. For some embodiments, the charge generating compound comprises oxytitanium phthalocyanine (e.g., any phase thereof), hydroxygallium phthalocyanine or a combination thereof.

[0042] The photoconductive layer of this invention may optionally contain a second charge transport material which may be a charge transport compound, an electron transport compound, or a combination of both. Generally, any charge transport compound or electron transport compound known in the art can be used as the second charge transport material.

[0043] An electron transport compound and a UV light stabilizer can have a synergistic relationship for providing desired electron flow within the photoconductor. The presence of the UV light stabilizers alters the electron transport properties of the electron transport compounds to improve the electron transporting properties of the composite. UV light stabilizers can be ultraviolet light absorbers or ultraviolet light inhibitors that trap free radicals.

[0044] UV light absorbers can absorb ultraviolet radiation and dissipate it as heat. UV light inhibitors are thought to trap free radicals generated by the ultraviolet light and after trapping of the free radicals, subsequently to regenerate active stabilizer moieties with energy dissipation. In view of the synergistic relationship of the UV stabilizers with electron transport compounds, the particular advantages of the UV stabilizers may not be their UV stabilizing abilities, although the UV stabilizing ability may be further advantageous in reducing degradation of the organophotoreceptor over time. The improved synergistic performance of organophotoreceptors with layers comprising both an electron transport compound and a UV stabilizer are described further in copending U.S. patent application Ser. No. 10/425,333 filed on Apr. 28, 2003 to Zhu, entitled “Organophotoreceptor With A Light Stabilizer,” incorporated herein by reference.

[0045] Non-limiting examples of suitable light stabilizer include, for example, hindered trialkylamines such as Tinuvin 144 and Tinuvin 292 (from Ciba Specialty Chemicals, Terrytown, N.Y.), hindered alkoxydialkylamines such as Tinuvin 123 (from Ciba Specialty Chemicals), benzotriazoles such as Tinuvan 328, Tinuvin 900 and Tinuvin 928 (from Ciba Specialty Chemicals), benzophenones such as Sanduvor 3041 (from Clariant Corp., Charlotte, N.C.), nickel compounds such as Arbestab (from Robinson Brothers Ltd, West Midlands, Great Britain), salicylates, cyanocinnamates, benzylidene malonates, benzoates, oxanilides such as Sanduvor VSU (from Clariant Corp., Charlotte, N.C.), triazines such as Cyagard UV-1164 (from Cytec Industries Inc., N.J.), polymeric sterically hindered amines such as Luchem (from Atochem North America, Buffalo, N.Y.). In some embodiments, the light stabilizer is selected from the group consisting of hindered trialkylamines having the following formula:

[0046] where R₁, R₂, R₃, R₄, R₆, R₇,R₈, R₁₀, R₁₁, R₁₂, R₁₃, R₁₄, R₁₅ are, each independently, hydrogen alkyl group, or ester, or ether group; and R₅, R₉, and R₁₄ are, each independently, alkyl group; and X is a linking group selected from the group consisting of —O—CO—(CH₂)_(m)—CO—O— where m is between 2 to 20.

[0047] The binder generally is capable of dispersing or dissolving the charge transport compound (in the case of the charge transport layer or a single layer construction) and/or the charge generating compound (in the case of the charge generating layer or a single layer construction). Examples of suitable binders for both the charge generating layer and charge transport layer generally include, for example, polystyrene-co-butadiene, polystyrene-co-acrylonitrile, modified acrylic polymers, polyvinyl acetate, styrene-alkyd resins, soya-alkyl resins, polyvinylchloride, polyvinylidene chloride, polyacrylonitrile, polycarbonates, polyacrylic acid, polyacrylates, polymethacrylates, styrene polymers, polyvinyl butyral, alkyd resins, polyamides, polyurethanes, polyesters, polysulfones, polyethers, polyketones, phenoxy resins, epoxy resins, silicone resins, polysiloxanes, poly(hydroxyether) resins, polyhydroxystyrene resins, novolak, poly(phenylglycidyl ether)-co-dicyclopentadiene, copolymers of monomers used in the above-mentioned polymers, and combinations thereof. Specific suitable binders include, for example, polyvinyl butyral, polycarbonate, and polyester. Non-limiting examples of polyvinyl butyral include BX-1 and BX-5 from Sekisui Chemical Co. Ltd., Japan. Non-limiting examples of suitable polycarbonate include polycarbonate A which is derived from bisphenol-A (e.g. Iupilon-A from Mitsubishi Engineering Plastics, or Lexan 145 from General Electric); polycarbonate Z which is derived from cyclohexylidene bisphenol (e.g. Iupilon-Z from Mitsubishi Engineering Plastics Corp, White Plain, N.Y.); and polycarbonate C which is derived from methylbisphenol A (from Mitsubishi Chemical Corporation). Non-limiting examples of suitable polyester binders include ortho-polyethylene terephthalate (e.g. OPET TR-4 from Kanebo Ltd., Yamaguchi, Japan).

[0048] Suitable optional additives for any one or more of the layers include, for example, antioxidants, coupling agents, dispersing agents, curing agents, surfactants, and combinations thereof.

[0049] The photoconductive element overall typically has a thickness from about 10 microns to about 45 microns. In the dual layer embodiments having a separate charge generating layer and a separate charge transport layer, charge generation layer generally has a thickness form about 0.5 microns to about 2 microns, and the charge transport layer has a thickness from about 5 microns to about 35 microns. In embodiments in which the charge transport material and the charge generating compound are in the same layer, the layer with the charge generating compound and the charge transport composition generally has a thickness from about 7 microns to about 30 microns. In embodiments with a distinct electron transport layer, the electron transport layer has an average thickness from about 0.5 microns to about 10 microns and in further embodiments from about 1 micron to about 3 microns. In general, an electron transport overcoat layer can increase mechanical abrasion resistance, increases resistance to carrier liquid and atmospheric moisture, and decreases degradation of the photoreceptor by corona gases. A person of ordinary skill in the art will recognize that additional ranges of thickness within the explicit ranges above are contemplated and are within the present disclosure.

[0050] Generally, for the organophotoreceptors described herein, the charge generation compound is in an amount from about 0.5 to about 25 weight percent, in further embodiments in an amount from about 1 to about 15 weight percent, and in other embodiments in an amount from about 2 to about 10 weight percent, based on the weight of the photoconductive layer. The charge transport material is in an amount from about 10 to about 80 weight percent, based on the weight of the photoconductive layer, in further embodiments in an amount from about 35 to about 60 weight percent, and in other embodiments from about 45 to about 55 weight percent, based on the weight of the photoconductive layer. The optional second charge transport material, when present, can be in an amount of at least about 2 weight percent, in other embodiments from about 2.5 to about 25 weight percent, based on the weight of the photoconductive layer, and in further embodiments in an amount from about 4 to about 20 weight percent, based on the weight of the photoconductive layer. The binder is in an amount from about 15 to about 80 weight percent, based on the weight of the photoconductive layer, and in further embodiments in an amount from about 20 to about 75 weight percent, based on the weight of the photoconductive layer. A person of ordinary skill in the art will recognize that additional ranges within the explicit ranges of compositions are contemplated and are within the present disclosure.

[0051] For the dual layer embodiments with a separate charge generating layer and a charge transport layer, the charge generation layer generally comprises a binder in an amount from about 10 to about 90 weight percent, in further embodiments from about 15 to about 80 weight percent and in some embodiments in an amount from about 20 to about 75 weight percent, based on the weight of the charge generation layer. The optional charge transport material in the charge generating layer, if present, generally can be in an amount of at least about 2.5 weight percent, in further embodiments from about 4 to about 30 weight percent and in other embodiments in an amount from about 10 to about 25 weight percent, based on the weight of the charge generating layer. The charge transport layer generally comprises a binder in an amount from about 20 weight percent to about 70 weight percent and in further embodiments in an amount from about 30 weight percent to about 50 weight percent. A person of ordinary skill in the art will recognize that additional ranges of binder concentrations for the dual layer embodiments within the explicit ranges above are contemplated and are within the present disclosure.

[0052] For the embodiments with a single layer having a charge generating compound and a charge transport material, the photoconductive layer generally comprises a binder, a charge transport material, and a charge generation compound. The charge generation compound can be in an amount from about 0.05 to about 25 weight percent and in further embodiments in an amount from about 2 to about 15 weight percent, based on the weight of the photoconductive layer. The charge transport material can be in an amount from about 10 to about 80 weight percent, in other embodiments from about 25 to about 65 weight percent, in additional embodiments from about 30 to about 60 weight percent and in further embodiments in an amount from about 35 to about 55 weight percent, based on the weight of the photoconductive layer, with the remainder of the photoconductive layer comprising the binder, and optional additives, such as any conventional additives. A single layer with a charge transport composition and a charge generating compound generally comprises a binder in an amount from about 10 weight percent to about 75 weight percent, in other embodiments from about 20 weight percent to about 60 weight percent, and in further embodiments from about 25 weight percent to about 50 weight percent. Optionally, the layer with the charge generating compound and the charge transport material may comprise a second charge transport material. The optional second charge transport material, if present, generally can be in an amount of at least about 2.5 weight percent, in further embodiments from about 4 to about 30 weight percent and in other embodiments in an amount from about 10 to about 25 weight percent, based on the weight of the photoconductive layer. A person of ordinary skill in the art will recognize that additional composition ranges within the explicit compositions ranges for the layers above are contemplated and are within the present disclosure.

[0053] In general, any layer with an electron transport compound can advantageously further include a UV light stabilizer. In particular, the electron transport layer generally can comprise an electron transport compound, a binder, and an optional UV light stabilizer. An overcoat layer comprising an electron transport compound is described further in copending U.S. patent application Ser. No. 10/396,536 to Zhu et al. entitled, “Organophotoreceptor With An Electron Transport Layer,” incorporated herein by reference. For example, an electron transport compound as described above may be used in the release layer of the photoconductors described herein. The electron transport compound in an electron transport layer can be in an amount from about 10 to about 50 weight percent, and in other embodiments in an amount from about 20 to about 40 weight percent, based on the weight of the electron transport layer. A person of ordinary skill in the art will recognize that additional ranges of compositions within the explicit ranges are contemplated and are within the present disclosure.

[0054] The UV light stabilizer, if present, in any one or more appropriate layers of the photoconductor generally is in an amount from about 0.5 to about 25 weight percent and in some embodiments in an amount from about 1 to about 10 weight percent, based on the weight of the particular layer. A person of ordinary skill in the art will recognize that additional ranges of compositions within the explicit ranges are contemplated and are within the present disclosure.

[0055] For example, the photoconductive layer may be formed by dispersing or dissolving the components, such as one or more of a charge generating compound, the charge transport material of this invention, a second charge transport material such as a charge transport compound or an electron transport compound, a UV light stabilizer, and a polymeric binder in organic solvent, coating the dispersion and/or solution on the respective underlying layer and drying the coating. In particular, the components can be dispersed by high shear homogenization, ball-milling, attritor milling, high energy bead (sand) milling or other size reduction processes or mixing means known in the art for effecting particle size reduction in forming a dispersion.

[0056] The photoreceptor may optionally have one or more additional layers as well. An additional layer can be, for example, a sub-layer or an overcoat layer, such as a barrier layer, a release layer, a protective layer, or an adhesive layer. A release layer or a protective layer may form the uppermost layer of the photoconductor element. A barrier layer may be sandwiched between the release layer and the photoconductive element or used to overcoat the photoconductive element. The barrier layer provides protection from abrasion to the underlayers. An adhesive layer locates and improves the adhesion between a photoconductive element, a barrier layer and a release layer, or any combination thereof. A sub-layer is a charge blocking layer and locates between the electrically conductive substrate and the photoconductive element. The sub-layer may also improve the adhesion between the electrically conductive substrate and the photoconductive element.

[0057] Suitable barrier layers include, for example, coatings such as crosslinkable siloxanol-colloidal silica coating and hydroxylated silsesquioxane-colloidal silica coating, and organic binders such as polyvinyl alcohol, methyl vinyl ether/maleic anhydride copolymer, casein, polyvinyl pyrrolidone, polyacrylic acid, gelatin, starch, polyurethanes, polyimides, polyesters, polyamides, polyvinyl acetate, polyvinyl chloride, polyvinylidene chloride, polycarbonates, polyvinyl butyral, polyvinyl acetoacetal, polyvinyl formal, polyacrylonitrile, polymethyl methacrylate, polyacrylates, polyvinyl carbazoles, copolymers of monomers used in the above-mentioned polymers, vinyl chloride/vinyl acetate/vinyl alcohol terpolymers, vinyl chloride/vinyl acetate/maleic acid terpolymers, ethylene/vinyl acetate copolymers, vinyl chloride/vinylidene chloride copolymers, cellulose polymers, and mixtures thereof. The above barrier layer polymers optionally may contain small inorganic particles such as fumed silica, silica, titania, alumina, zirconia, or a combination thereof. Barrier layers are described further in U.S. Pat. No. 6,001,522 to Woo et al., entitled “Barrier Layer For Photoconductor Elements Comprising An Organic Polymer And Silica,” incorporated herein by reference. The release layer topcoat may comprise any release layer composition known in the art. In some embodiments, the release layer is a fluorinated polymer, siloxane polymer, fluorosilicone polymer, silane, polyethylene, polypropylene, polyacrylate, or a combination thereof. The release layers can comprise crosslinked polymers.

[0058] The release layer may comprise, for example, any release layer composition known in the art. In some embodiments, the release layer comprises a fluorinated polymer, siloxane polymer, fluorosilicone polymer, polysilane, polyethylene, polypropylene, polyacrylate, poly(methyl methacrylate-co-methacrylic acid), urethane resins, urethane-epoxy resins, acrylated-urethane resins, urethane-acrylic resins, or a combination thereof. In further embodiments, the release layers comprise crosslinked polymers.

[0059] The protective layer can protect the organophotoreceptor from chemical and mechanical degradation. The protective layer may comprise any protective layer composition known in the art. In some embodiments, the protective layer is a fluorinated polymer, siloxane polymer, fluorosilicone polymer, polysilane, polyethylene, polypropylene, polyacrylate, poly(methyl methacrylate-co-methacrylic acid), urethane resins, urethane-epoxy resins, acrylated-urethane resins, urethane-acrylic resins, or a combination thereof. In some embodiments of particular interest, the release layers are crosslinked polymers.

[0060] An overcoat layer may comprise an electron transport compound as described further in copending U.S. patent application Ser. No. 10/396,536, filed on Mar. 25, 2003 to Zhu et al. entitled, “Organoreceptor With An Electron Transport Layer,” incorporated herein by reference. For example, an electron transport compound, as described above, may be used in the release layer of this invention. The electron transport compound in the overcoat layer can be in an amount from about 2 to about 50 weight percent, and in other embodiments in an amount from about 10 to about 40 weight percent, based on the weight of the release layer. A person of ordinary skill in the art will recognize that additional ranges of composition within the explicit ranges are contemplated and are within the present disclosure.

[0061] Generally, adhesive layers comprise a film forming polymer, such as polyester, polyvinylbutyral, polyvinylpyrrolidone, polyurethane, polymethyl methacrylate, poly(hydroxy amino ether) and the like. Barrier and adhesive layers are described further in U.S. Pat. No. 6,180,305 to Ackley et al., entitled “Organic Photoreceptors for Liquid Electrophotography,” incorporated herein by reference.

[0062] Sub-layers can comprise, for example, polyvinylbutyral, organosilanes, hydrolyzable silanes, epoxy resins, polyesters, polyamides, polyurethanes, cellulosics, and the like. In some embodiments, the sub-layer has a dry thickness between about 20 Angstroms and about 20,000 Angstroms. Sublayers containing metal oxide conductive particles can be between about 1 and about 25 microns thick. A person of ordinary skill in the art will recognize that additional ranges of compositions and thickness within the explicit ranges are contemplated and are within the present disclosure.

[0063] The charge transport materials as described herein, and photoreceptors including these compounds, are suitable for use in an imaging process with either dry or liquid toner development. For example, any dry toners and liquid toners known in the art may be used in the process and the apparatus of this invention. Liquid toner development can be desirable because it offers the advantages of providing higher resolution images and requiring lower energy for image fixing compared to dry toners. Examples of suitable liquid toners are known in the art. Liquid toners generally comprise toner particles dispersed in a carrier liquid. The toner particles can comprise a colorant/pigment, a resin binder, and/or a charge director. In some embodiments of liquid toner, a resin to pigment ratio can be from 1:1 to 10:1, and in other embodiments, from 4:1 to 8:1. Liquid toners are described further in Published U.S. patent applications Ser. No. 2002/0128349, entitled “Liquid Inks Comprising A Stable Organosol,” and U.S. patent application Ser. No. 2002/0086916, entitled “Liquid Inks Comprising Treated Colorant Particles,” and U.S. Pat. No. 6,649,316, entitled “Phase Change Developer For Liquid Electrophotography,” all three of which are incorporated herein by reference.

[0064] Charge Transport Material

[0065] As described herein, an organophotoreceptor comprises a charge transport material having the formula

[0066] where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group such as a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent comprising a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group.

[0067] With respect to Formula (1), substitution is liberally allowed, especially on the 9-fluorenylidene group and the arylamine group. Variation of the substituents on the those groups can result in various physical effects on the properties of the compounds, such as mobility, solubility, compatibility, stability, spectral absorbance, dispersibility, and the like, including, for example, substitutions known in the art to effect particular modifications.

[0068] In some embodiments, the organophotoreceptor may comprise a charge transport material having the formula

[0069] where X comprises an arylamine group such as a p-(N,N-disubstituted)arylarnine group, a carbazole group, or a julolidine group; R₆ comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; R₇ comprises a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group; and R₈ comprises a hydrogen, a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, or an aromatic group.

[0070] Specific, non-limiting examples of suitable charge transport materials within the general structure of the present invention have the following structures.

[0071] Synthesis of Charge Transport Materials

[0072] The synthesis of the charge transport materials of this invention can be prepared by the following multi-step synthetic procedure, although other suitable procedures can be used by a person of ordinary skill in the art based on the disclosure herein.

[0073] A suitable first step is the reaction between a 9-fluorenone compound with hydrazine, NH₂NH₂, in a molar ratio of about 1:1 to form the corresponding hydrazone. The next step is the reaction between the hydrazone and an arylamine having an aldehyde group or a keto group to form an azine compound having an arylamine group and a 9-fluorenylidene group. The arylamine having an aldehyde group or a keto group can be prepared by Vilsmeier-Haack acylation by reacting the corresponding arylamine with a mixture of phosphorus oxychloride (POCl₃) and a dialkylamide, such as N,N-dimethylformamide. The Vilsmeier-Haack acylation and related reactions are described in Carey et al., “Advanced Organic Chemistry, Part B: Reactions and Synthesis,” New York, 1983, pp. 380-393, incorporated herein by reference. In some embodiments, the order of these two reactive steps can be reversed.

[0074] To form the specific ester compounds of formulas (2)-(6), initially a 9-fluorenone carboxylic acid reacts with a selected alcohol to form the corresponding alkyl 9-fluorenone-carbaoxylate ester. Then the alkyl 9-fluorenone-carboxylateester reacts with hydrazine, NH₂NH₂, and an arylamine having an aldehyde group, as described above. Further details are presented in the examples below.

[0075] The invention will now be described further by way of the following examples.

EXAMPLES

[0076] Synthesis of Comparative Charge Transport Material

[0077] Compounds (2)-(6) are found to be suitable for use as charge transport materials, especially as a charge transport compound for transporting hole carriers. In the comparative examples below, (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile was used as a comparing electron transport compound. The synthesis of (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile is described below.

[0078] Preparation of (4-n-Butoxycarbonyl-9-fluorenylidene)malononitrile

[0079] A mixture of 9-fluorenone-4-carboxylic acid (70 g, 0.312 mole, from Sigma-Aldrich, Milwaukee, Wis.), n-butanol (480 g, 6.5 mole, from Fisher Scientific Company Inc., Hanover Park, Ill.), toluene (1000 ml), and concentrated sulfiric acid (4 ml) was added to a 2-liter round bottom flask equipped with a mechanical stirrer and a reflux condenser with a Dean Stark apparatus. With aggressive agitation, the solution was refluxed for 5 hours, during which time ˜6 g of water were collected in the Dean Stark apparatus. After refluxing, the flask was cooled to room temperature. The solvents were evaporated and the residue was added with agitation to 4-liter of a 3% aqueous solution of sodium bicarbonate. The solid was filtered off, washed with water until the pH of the washed water was neutral, and dried in the hood overnight. The product was n-butyl fluorenone-4-carboxylate ester. The yield was 70 g (80%). A ¹H-NMR spectrum of n-butyl fluorenone-4-carboxylate ester was obtained in CDCl₃ with a 300 MHz NMR from Bruker Instrument. The ¹H NMR spectrum was characterized by the following chemical shifts (δ, ppm): 0.87-1.09 (t, 3H); 1.42-1.70 (m, 2H); 1.75-1.88 (q, 2H4.26-4.64 (t, 2H); 7.29-7.45 (m, 2H); 7.46-7.58 (m, 1H); 7.60-7.68 (dd, 1H); 7.75 -7.82 (dd, 1H); 7.90-8.00 (dd, 1H); and 8.25-8.35 (dd, 1H).

[0080] A mixture of 70 g (0.25 mole) of n-butyl fluorenone-4-carboxylate ester, 750 ml of absolute methanol, 37 g (0.55 mole) of malononitrile (from Sigma-Aldrich, Milwaukee, Wis.), 20 drops of piperidine (from Sigma-Aldrich, Milwaukee, Wis.) was added to a 2-liter, 3-neck round bottom flask equipped with a mechanical stirrer and a reflux condenser. The solution was refluxed for 8 hours and the flask was cooled to room temperature. The orange crude product was filtered, washed twice with 70 ml of methanol and once with 150 ml of water, and dried overnight in a hood. This orange crude product was recrystallized from a mixture of 600 ml of acetone and 300 ml of methanol using activated charcoal. The flask was placed at 0° C. for 16 hours. The crystals formed were filtered and dried in a vacuum oven at 50° C. for 6 hours to obtain 60 g of pure (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile. The melting point of the solid was found to be 99-100° C. A ¹H-NMR spectrum of (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile was obtained in CDCl₃ with a 300 MHz NMR from Bruker Instrument. The ¹H-NMR spectrum was characterized by the following chemical shifts (δ, ppm): 0.74-1.16 (t, 3H); 1.38-1.72 (m, 2H); 1.70-1.90 (q, 2H); 4.29-4.55 (t, 2H); 7.31-7.43 (m, 2H); 7.45-7.58 (m, 1H); 7.81-7.91 (dd, 1H); 8.15-8.25 (dd, 1H); 8.42-8.52 (dd, 1H); and 8.56-8.66 (dd, 1H).

Example 1

[0081] Synthesis and Characterization Charge Transport Materials

[0082] This example described the synthesis and characterization of Compounds (2)-(6) in which the numbers refer to the formula numbers above. The characterization involves chemical characterization, while the electrostatic characterization of materials formed with the compounds are described in subsequent examples.

[0083] Compound (2)

[0084] A mixture of 56 g of n-butyl fluorenone-4-carboxylate ester (0.2 mole, prepared in the first step), 200 ml of ethanol, 12.82 g of anhydrous hydrazine (0.4 mole, from Aldrich Chemicals, Milwaukee, Wis.) was added to a 500 ml 3-neck round bottom flask equipped with a mechanical stirrer and a reflux condenser. The flask was heated at 74° C. for 5 hours. The solution was kept at 0° C. overnight. The yellow solid that formed was filtered off, washed with 50 ml of ethanol, and dried at 50° C. in a vacuum oven for 8 hours. The product was n-butyl (9-fluorenylidene)hydrazone-4-carboxylate ester. The yield was 49 g (83% yield). The ¹H-NMR spectrum (300 MHz) of the product in CDCl₃ was characterized by the following chemical shifts (δ, ppm): 0.93-1.06 (t, 3H); 1.42-1.62 (m, 2H); 1.73-1.89 (q, 2H); 4.36-4.51 (t, 2H); 6.38-6.55 (NH₂, two broad singlets); and 6.38-8.50 (aromatic protons).

[0085] A mixture of n-butyl (9-fluorenylidene)hydrazone-4-carboxylate ester (12 g, 0.04 mole, prepared in previous step), 100 ml of ethanol, (4-diphenylamino)benzaldeyhde (11.14 g, 0.04 mole, from Fluka Co.), and 2 drops of 37% aqueous hydrochloric acid was added to a 500 ml 3-neck round bottom flask equipped with a reflux condenser and a mechanical stirrer. The solution was refluxed for one-half of an hour. The crude product was isolated by evaporating the solvent and was recrystallized 4 times from a mixture of tetrahydrofuran and ethanol with activated charcoal. The orange product was filtered off and dried at 50° C. in a vacuum oven for 8 hours. The yield of Compound (2) was 8.7 g (40%). The ¹H-NMR spectrum (300 MHz) of Compound (2) in CDCl₃ was characterized by the following chemical shifts (δ, ppm): 0.94-1.05 (t, 3H); 1.43-1.59 (m, 2H); 1.74-1.88 (q, 2H); 4.38-4.48 (t, 2H); and 7.06-8.92 (aromatic protons).

[0086] Compound (3)

[0087] Compound (3) was prepared similarly to Compound (2) except that n-ethyl-3-carbazole carboxaldehyde (from Aldrich Chemicals, Milwaukee, Wis.) replaced (4-diphenylamino)benzaldeyhde. An orange solid was obtained. The yield was 7 g (35%). The ¹NMR spectrum (300 MHz) of Compound (3) in CDCl₃ was characterized by the following chemical shifts (δ, ppm): 0.94-1.07 (t, 3H); 1.43-1.60 (m, 2H); 1.74-1.90 (q, 2H); 437-4.50 (t, 2H); and 7.27-8.84 (aromatic protons).

[0088] Compound (4)

[0089] Compound (4) can be prepared similarly to Compound (2) except that n-penthyl-3-carbazole carboxaldehyde (prepared according to the procedure below) replaces (4-diphenylamino)benzaldeyhde.

[0090] A mixture of carbazole (250 g, 1.5 mole, from Aldrich, Milwaukee, Wis.), 1-bromoheptane (242 g, 1.6 mole, from Aldrich, Milwaukee, Wis.), benzyltriethylammonium chloride (17 g, 0.075 mole, from Aldrich, Milwaukee, Wis.), 1 liter of toluene, and 600 g of 50% aqueous sodium hydroxide was added to a 3-liter 3-neck round bottom flask equipped with a mechanical stirrer and a reflux condenser. The flask was stirred at room temperature for a period of one-half of an hour and then refluxed for 5 hours. When thin layer chromotography showed that the starting material had disappeared and the product had formed, the flask was cooled to room temperature. The organic phase was separated and washed several times with water until the pH of the washed water was neutral. The organic phase was dried over magnesium sulfate and filtered, and the solvent was evaporated. The yield was 320 g (90%).

[0091] A mixture of n-pentylcarbazole (320 g, 1.35 mole) and 600 ml of dimethylformamide was added to a 2-liter 3-neck round bottom flask equipped with a reflux condenser and a mechanical stirrer. The flask was cooled on an ice bath. When the solution temperature reached 0° C., phosphorous oxychloride (1.5 mole, 230 g, from Aldrich, Milwaukee, Wis.) was added dropwise using an addition funnel. The temperature inside the flask was kept at below 5° C. during the addition of phosphorous oxychloride. When the addition of phosphorous oxychloride was completed, the flask was placed in a steam bath for 2 hours. Then, the flask was cooled to room temperature and the contents were added to a large excess of water. The solid was filtered off and washed repeatedly with water until the pH of the washed water was neutral. The product, Compound (4), was dried in a vacuum oven at 50° C. for 4 hours. The yield was 286 g (80%).

[0092] Compound (5)

[0093] Compound (5) can be prepared similarly to Compound (2) except that n-ethyl fluorenone-4-carboxylate ester replaces n-butyl fluorenone-4-carboxylate ester. The n-ethyl fluorenone-4-carboxylate ester is prepared similar to n-butyl fluorenone-4-carboxylate ester except that ethanol replaces n-butanol.

[0094] Compound (6)

[0095] Compound (6) can be prepared similarly to Compound (2) except that julolidine aldehyde (prepared according to the procedure described below) replaces 4-(diphenylamino)benzaldehyde.

[0096] A mixture of julolidine (100 g, 0.6 moles, from Aldrich, Milwaukee, Wis.) and 200 ml of N,N-dimethylformamide (DMF, commercially obtained from Aldrich) is added to a 500 ml three neck round bottom flask. After julolidine is dissolved, the flask is cooled to 0° C. in an ice bath. Then, phosphorous oxychloride (107 g, 0.7 mole, available from Aldrich) is added dropwise via an addition funnel while the temperature is kept below 5° C. After the addition of phosphorous oxychloride is completed, the flask is warmed to room temperature and placed in a steam bath where it is stirred for 1 hour. The flask is then cooled to room temperature, and the solution is added slowly with good agitation to a large excess of distilled water. Stirring is continued for an additional 2 hours. The solid julolidine aldehyde is filtered off and washed repeatedly with water until the pH of the washed water becomes neutral. The product can be dried at 50° C. in a vacuum oven for 4 hours.

Example 2

[0097] Preparation of Organophotoreceptors

[0098] Conveniently, the photoconductive element may be formed by dispersing or dissolving the components, such as a charge generating compound, a charge transport compound, a light stabilizer, an electron transport compound, and/or a polymeric binder in organic solvent, coating the dispersion and/or solution on the respective underlying layer and drying the coating. In some embodiments, the components can be dispersed by high shear homogenization, ball-milling, attritor milling, high energy bead (sand) milling or other size reduction processes or mixing means known in the art for effecting particle size reduction in forming a dispersion. The coatings can be applied, for example, using knife coating, extrusion, dip coating or other appropriate coating approaches, including those known in the art. In some embodiments, a plurality of layers can be applied as sequential coatings. The layers can be dried prior to the application of a subsequent layer. Some specific examples are presented below.

[0099] The examples below further describes the preparation of organophotoreceptor samples. The samples include two organophotoreceptor samples with Compounds (2) and (3) and two comparative organophotoreceptor samples prepared with (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile.

[0100] Sample 1

[0101] Sample (1) was a single layer organophotoreceptor having a 76.2 micron (3 mil) thick polyester substrate having a layer of vapor-coated aluminum (obtained from CP Films, Martinsville, Va.). The coating solution for the single layer organophotoreceptor was prepared by pre-mixing 2.4 g of 20 wt. % Compound (2) in tetrahydrofuran, 6.66 g of 25 wt. % MPCT-10 (a charge transfer material, obtained from Mitsubishi Paper Mills, Tokyo, Japan) in tetrahydrofuran, 7.65 g of 12 wt. % polyvinyl butyral resin (BX-1, obtained from Sekisui Chemical Co. Ltd., Japan) in tetrahydrofuran. A 0.74 g quantity of a CGM mill-base containing 19 wt. % of titanyl oxyphthalocyanine and a polyvinyl butyral resin (BX-5, obtained from Sekisui Chemical Co. Ltd., Japan) in a ratio of 2.3:1 was then added to the mixture. The CGM mill-base was obtained by milling 112.7 g of titanyl oxyphthalocyanine (obtained from H.W. Sands Corp., Jupiter, Fla.) with 49 g of polyvinyl butyral resin (BX-5) in 651 g of MEK on a horizontal sand mill (model LMC12 DCMS, obtained from Netzsch Incorporated, Exton, Pa.) with 1-micron zirconia beads using recycle mode for 4 hours. After mixing on a mechanical shaker for ˜1 hour, the single layer coating solution was coated onto the substrate described above using a knife coater with an orifice set to 94 microns. The coating was dried in an oven at no 110° C. for 5 minutes.

[0102] Sample (2)

[0103] Sample (2) was prepared similarly according to the procedure for Sample 1 except that Compound (3) replaced Compound (2).

[0104] Comparative Sample A

[0105] Comparative Sample A was prepared similarly according to the procedure for Sample 1 except that (4-n-butoxycarbonyl-9-fluorenylidene)malononitrile replaced Compound (2).

[0106] Sample 3

[0107] Sample 3 was prepared similarly according to the procedure for Comparative Sample A except that Compound (2) replaced MPCT-10.

Example 3

[0108] Electrostatic Testing and Properties of Organophotoreceptors

[0109] This example provides results of electrostatic testing on the organophotoreceptor samples formed as described in Example 1.

[0110] Electrostatic cycling performance of organophotoreceptors described herein with azine compounds can be determined using in-house designed and developed test bed that is capable of testing, for example, the sample strips wrapped around a 160 mm drum. The results on these samples are indicative of results that would be obtained with other support structures, such as belts, drums and the like, for supporting the organophotoreceptors.

[0111] For testing using a 160 mm drum, three coated sample strips, each measuring 50 cm long by 8.8 cm wide, are fastened side-by-side and completely around an aluminum drum (50.3 cm circumference). In some embodiments, at least one of the strips is a comparative sample that is precision web coated and used as an internal reference point. In this electrostatic cycling tester, the drum rotated at a rate of 8.13 cm /sec (3.2 ips), and the location of each station in the tester (distance and elapsed time per cycle) is given as shown in the following table: TABLE 1 Electrostatic test stations around the 160 mm drum at 8.13 cm/sec. Total Distance, Total Time, Station Degrees cm sec Front erase bar edge  0° Initial, 0 cm Initial, 0 s Erase Bar    0-7.2°   0-1.0   0-0.12 Scorotron Charger 113.1-135.3° 15.8-18.9 1.94-2.33 Laser Strike 161.0° 22.5 2.77 Probe #1 181.1° 25.3 3.11 Probe #2 251.2° 35.1 4.32 Erase bar 360° 50.3 6.19

[0112] The erase bar is an array of laser emitting diodes (LED) with a wavelength of 720 nm that discharges the surface of the organophotoreceptor. The scorotron charger comprises a wire that permits the transfer of a desired amount of charge to the surface of the organophotoreceptor.

[0113] From the above table, the first electrostatic probe (TREK 344™ electrostatic meter, Trek, Inc. Medina, N.Y.) is located 0.34 s after the laser strike station and 0.78 s after the scorotron while the second probe (TREK™ 344 electrostatic meter) is located 1.21 s from the first probe and 1.99 s from the scorotron. All measurements are performed at ambient temperature and relative humidity.

[0114] Electrostatic measurements were obtained as a compilation of several runs on the test station. The first three diagnostic tests (prodtest initial, VlogE initial, dark decay initial) are designed to evaluate the electrostatic cycling of a new, fresh sample and the last three, identical diagnostic test (prodtest final, VlogE final, dark decay final) are run after cycling of the sample. In addition, measurements were made periodically during the test, as described under “longrun” below. The laser is operated at 780 nm wavelength, 600 dpi, 50 micron spot size, 60 nanoseconds/pixel expose time, 1,800 lines per second scan speed, and a 100% duty cycle. The duty cycle is the percent exposure of the pixel clock period, i.e., the laser is on for the full 60 nanoseconds per pixel at a 100% duty cycle.

[0115] Electrostatic Test Suite:

[0116] 1) PRODTEST: Charge acceptance (V_(acc)) and discharge voltage (V_(dis)) were established by subjecting the samples to corona charging (erase bar always on) for three complete drum revolutions (laser off); discharged with the laser @ 780 nm & 600 dpi on the forth revolution (50 um spot size, expose 60 nanoseconds/pixel, run at a scan speed of 1,800 lines per second, and use a 100% duty cycle); completely charged for the next three revolutions (laser off); discharged with only the erase lamp @ 720 nm on the eighth revolution (corona and laser off) to obtain residual voltage (V_(res)); and, finally, completely charged for the last three revolutions (laser off). The contrast voltage (V_(con)) is the difference between V_(acc) and V_(dis) and the functional dark decay (V_(dd)) is the difference in charge acceptance potential measured by probes #1 and #2.

[0117] 2) VLOGE: This test measures the photoinduced discharge of the photoconductor to various laser intensity levels by monitoring the discharge voltage of the sample as a function of the laser power (exposure duration of 50 ns) with fixed exposure times and constant initial potentials. This test measures the photoinduced discharge of the photoconductor to various laser intensity levels by monitoring the discharge voltage of the sample as a function of the laser power (exposure duration of 50 ns) with fixed exposure times and constant initial potentials. The functional photosensitivity, S_(780 nm), and operational power settings can be determined from this diagnostic test.

[0118] 3) DARK DECAY: This test measures the loss of charge acceptance in the dark with time without laser or erase illumination for 90 seconds and can be used as an indicator of i) the injection of residual holes from the charge generation layer to the charge transport layer, ii) the thermal liberation of trapped charges, and iii) the injection of charge from the surface or aluminum ground plane.

[0119] 4) LONGRUN: The sample was electrostatically cycled for 100 drum revolutions according to the following sequence per each sample-drum revolution. The sample was charged by the corona, the laser was cycled on and off (80-100° sections) to discharge a portion of the sample and, finally, the erase lamp discharged the whole sample in preparation for the next cycle. The laser was cycled so that the first section of the sample was never exposed, the second section was always exposed, the third section was never exposed, and the final section was always exposed. This pattern was repeated for a total of 100 drum revolutions, and the data was recorded after every 5th cycle for the 100 cycle longrun.

[0120] 5) After the LONGRUN test, the PRODTEST, VLOGE, DARK DECAY diagnostic tests were run again.

[0121] The following Tables shows the results from the prodtest initial and prodtest final diagnostic tests. The values for the charge acceptance voltage (Vacc, probe #1 average voltage obtained from the third cycle), discharge voltage (Vdis, probe #1 average voltage obtained from the fourth cycle) are reported for the initial and final cycles. TABLE 2 Dry Electrostatic Test Results after 100 cycles. Prodtest Initial Prodtest Final Sample V_(acc) V_(dis) V_(con) S_(780 nm) V_(res) V_(acc) V_(dis) V_(con) V_(res) Sample 1 853 90 763 222 34 564 62 502 29 Sample 2 840 92 748 199 34 587 65 522 31 Sample 3 727 191  536 164 96 614 228  386 122  Comparative Sample A 905 61 844 210 21 618 58 560 22

[0122] In the above table, the radiation sensitivity (Sensitivity at 780 nm in m²/J) of the xerographic process was determined from the information obtained during the VLOGE diagnostic run by calculating the reciprocal of the product of the laser power required to discharge the photoreceptor to ½ of its initial potential, the exposure duration, and 1/spot size.

[0123] As understood by those skilled in the art, additional substitution, variation among substituents, and alternative methods of synthesis and use may be practiced within the scope and intent of the present disclosure of the invention. The embodiments above are intended to be illustrative and not limiting. Additional embodiments are within the claims. Although the present invention has been described with reference to particular embodiments, workers skilled in the art will recognize that changes may be made in form and detail without departing from the spirit and scope of the invention 

What is claimed is:
 1. An organophotoreceptor comprising an electrically conductive substrate and a photoconductive element on the electrically conductive substrate, the photoconductive element comprising: a) a charge transport material having the following formula:

where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent, wherein the solubilizing substituent comprises a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group; and (b) a charge generating compound.
 2. An organophotoreceptor according to claim 1 wherein X comprises a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group.
 3. An organophotoreceptor according to claim 1 wherein the solubilizing substituent comprises a —C(═O)O—R₅ group where R₅ is an alkyl group, an alkenyl group, or an aromatic group.
 4. An organophotoreceptor according to claim 1 wherein the 9-fluorenylidene group further comprises at least a substituent selected from the group consisting of a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, and an aromatic group.
 5. An organophotoreceptor according to claim 1 wherein the photoconductive element further comprises a second charge transport material.
 6. An organophotoconductor according to claim 5 wherein the second charge transport material comprises an electron transport compound.
 7. An organophotoreceptor according to claim 1 wherein the organophotoreceptor is in the form of a drum or a belt.
 8. An electrophotographic imaging apparatus comprising: (a) a light imaging component; and (b) an organophotoreceptor oriented to receive light from the light imaging component, the organophotoreceptor comprising an electrically conductive substrate and a photoconductive element on the electrically conductive substrate, the photoconductive element comprising: (i) a charge transport material having the formula

where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent, wherein the solubilizing substituent comprises a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group; and (ii) a charge generating compound.
 9. An electrophotographic imaging apparatus according to claim 8 wherein X comprises a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group.
 10. An electrophotographic imaging apparatus according to claim 8 wherein the solubilizing substituent comprises a —C(═O)O—R₅ group where R₅ is an alkyl group, an alkenyl group, or an aromatic group.
 11. An electrophotographic imaging apparatus according to claim 8 wherein the 9-fluorenylidene group further comprises at least a substituent selected from the group consisting of a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, and an aromatic group.
 12. An electrophotographic imaging apparatus according to claim 8 wherein the photoconductive element further comprises a second charge transport material.
 13. An electrophotographic imaging apparatus according to claim 12 wherein the second charge transport material comprises an electron transport compound.
 14. An electrophotographic imaging apparatus according to claim 8 further comprising a toner dispenser.
 15. An electrophotographic imaging process comprising: (a) applying an electrical charge to a surface of an organophotoreceptor comprising an electrically conductive substrate and a photoconductive element on the electrically conductive substrate, the photoconductive element comprising (i) a charge transport material having the following formula,

where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent, wherein the solubilizing substituent comprises a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group; and (ii) a charge transport compound; (b) imagewise exposing said surface of said organophotoreceptor to radiation to dissipate charge in selected areas and thereby form a pattern of charged and uncharged areas on said surface; (c) contacting said surface with a toner to create a toned image; and (d) transferring said toned image to a substrate.
 16. An electrophotographic imaging process according to claim 15 wherein X comprises a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group.
 17. An electrophotographic imaging process according to claim 15 wherein the solubilizing substituent comprises a —C(═O)O—R₅ group where R₅ is an alkyl group, an alkenyl group, or an aromatic group.
 18. An electrophotographic imaging process according to claim 15 wherein the 9-fluorenylidene group further comprises at least a substituent selected from the group consisting of a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, and an aromatic group.
 19. An electrophotographic imaging process according to claim 15 wherein the photoconductive element further comprises a second charge transport material.
 20. An electrophotographic imaging process according to claim 19 wherein the second charge transport material comprises an electron transport compound.
 21. A charge transport material having the following formula,

where R comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; X comprises an arylamine group; and Y comprises a 9-fluorenylidene group having at least a solubilizing substituent, wherein the solubilizing substituent comprises a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CR_(c)R_(d) group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group.
 22. A charge transport material according to claim 21 wherein X comprises a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group.
 23. A charge transport material according to claim 21 wherein the solubilizing substituent comprises a —C(═O)O—R₅ group where R₅ is an alkyl group, an alkenyl group, or an aromatic group.
 24. A charge transport material according to claim 21 wherein the 9-fluorenylidene group further comprises at least a substituent selected from the group consisting of a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, and an aromatic group.
 25. A charge transport material according to claim 21 wherein the charge transport material has formula:

where R₆ comprises a hydrogen, an alkyl group, an alkenyl group, a heterocyclic group, or an aromatic group; R₇ comprises a —(CH₂)_(n)H group where n is an integer between 1 and 50, and one or more of the methylene groups is optionally replaced by O, S, N, C, B, Si, P, C═O, O═S═O, a heterocyclic group, an aromatic group, an NR_(a) group, a CR_(b) group, a CRRD group, or a SiR_(e)R_(f) where R_(a), R_(b), R_(c), R_(d), R_(e), and R_(f) are, each independently, a bond, H, a hydroxyl group, a thiol group, a carboxyl group, an amino group, an alkyl group, an alkoxy group, an alkenyl group, a heterocyclic group, an aromatic group, or part of a ring group; R₈ comprises a hydrogen, a halogen, a NO₂ group, a cyano group, a hydroxyl group, a thiol group, a carboxyl group, an amine group, an ester group, an alkyl group, an alkoxy group, an alkenyl group, or an aromatic group; and X comprises an arylamine group.
 26. A charge transport material according to claim 25 wherein R₈ is a hydrogen and R₇ comprises a —C(═O)O—R₁₃ group where R₁₃ is an alkyl group, an alkenyl group, or an aromatic group.
 27. A charge transport material according to claim 25 wherein X comprises a p-(N,N-disubstituted)arylamine group, a carbazole group, or a julolidine group. 